A. Lime
B. Basic
C. Acid
D. None of these
Related Mcqs:
- 10 to 30% magnesite is added to Chromite to produce chrome-magnesite refractories. Magnesite addition is mainly done to improve the _____________ of Chromite?
A. Spalling resistance
B. Refractoriness
C. Crushing strength
D. Resistance to slag - Resistance to slag attack of a refractory _____________________?
A. Depends on the nature of slag & refractory
B. Decreases at higher temperature
C. Decreases, if defective joints & cracks exist in the refractory
D. All A., B. and C. - Firing temperature of magnesite bricks is about _____________ °C?
A. 800-1000
B. 1000-1200
C. 1600-1800
D. 2400-2600 - Maximum apparent porosity of magnesite bricks is about _____________ percent?
A. 8
B. 24
C. 44
D. 58 - Dolomite bricks have good resistance to attack by_____________________?
A. Molten steel
B. Iron oxide
C. Lime slag
D. None of these - Rate of slag attack on refractories increases with rise in temperature due to the___________________?
A. Decreased viscosity of slag
B. Increased thermal conductivity of brick
C. Oxidising condition in the furnace
D. None of these - Chrome magnesite bricks are_________________?
A. Acidic in nature
B. Neutral in nature
C. Having higher RUL than silica bricks
D. Made by mixing 30% Chromite and 70% Periclase - Magnesite chrome bricks are used in the___________________?
A. Roof lining of basic open hearth & other basic furnaces
B. Reheating furnaces
C. Soaking pits
D. All A., B. and C. - Which of the following impurities reduces the refractoriness of magnesite bricks ?
A. Al2O3
B. CaO
C. SiO2
D. All A., B. & C. - Magnesite bricks are used in those parts of furnaces, which are __________________?
A. Subjected to temperature fluctuation
B. Required to resist corrosive basic slag
C. Subjected to high load
D. None of these